Heat Treatment Salts

Product Description

INTRODUCTION

Salt       baths      have    many      advantages      over     other       heat       treatment      processes,    viz  Rapid    rate  of   heat   transfer in   the  salt   bath   gives   higher  output

Uniform      and   accurate    control      of    temperature     can    be    available    through   out  the bath   and   the   components.

The following   Salts   for   various   processes   of      Heat      Treatment   are    available     with     us.

SALTSFOR CARBURISING

ALFACARB “I

Salt   for     Carburising  with  Working Range 760-950C (ICI   Equivalent “`Rapicarb-H™)

ALFA CARB “II

Salt forCarburising with WorkingRange 800-950C (ICI Equivalent - `Rapicarb-S™ )

B.   NEUTRAL SALTS

ALFA 660   Working Range  660-900C ( ICI  Equivalent -  `NC  660™ )

ALFA 660 is usedfor  hardening various tool  steels,  preheating   high-speed  steels hot work          

Steels    prior   to   hardening    with ALFA 970.   ALFA 660    is  denser    than    ALFA 720,  but less    soluble   in  water.  ALFA   660  does   not   ecarburize   the   charge.  The  working  range 

can    be   increased   upto 1000 C  by   covering  the    molten   salt  with  ALFA

ECONOMISER. (225  gm per 100 kg ).

ALFA  720  Working Range  720 “ 900C (  ICI  Equivalent - WS  720  )

ALFA  720 is  a  salt   which  neither   carburise   nor   ecarburize   the steel and  it  readily dissolves in water.

ALFA 830    Working   Range  830 “ 1100 C ( ICI  Equivalent “ HT 830 )

ALFA 830    along   with     ALFA  ECONOMISER  (130gm  per 100 kg )    can    be    used     for hardening  tool   steel,  hot   working  dies,   high   Cr   steel    etc.   ALFA  830    can      be   used    safely    in ceramic       lined   electric    ecarburi   furnace. The floating  ALFA ECONOMISER  on the surface can    be mixed   by   stirring   with   a stirrer.The bath  can  bedesludged  for   every   8 hours  and    topped  up   with   ALFA 830   and     ALFA ECONOMISER    in   proportion.

ALFA  970  Working Range  970 “ 1350C ( ICI  Equivalent “ HS  970 )

ALFA  970  can   be    used   to  harden   high- speed, hot  working,  tool  steels   etc.   ALFA 970  neither   ecarburize   nor   allow     the  formation   of    scale on   the  surface of the  components.

C .   SALTS FOR QUENCHING AND TEMPERING

ALFA  540  Working Range  540-700C ( ICIEquivalent “ QS  540 )

ALFA  540  can      be     used   for    minimum    distortion     and   less    risk   of   cracks  than  in oil quenching.

ALFA  495  Working Range  495 “ 700C  ( ICI Equivalent “ QS  495 )

ALFA  330  Working Range  330 “ 535C  (ICI Equivalent  -  TS  330  )

ALFA  330   can    be     used    for    the    heat    treatment   of    ALUMINIUM  ALLOYS.  After solutionising      in    ALFA 330,      the   same    can   be   precipitation   hardened  in  ALFA  150.

10.  ALFA ECONOMISER   ( Refer  above )

11.  ALFA 220   Working Range  220 “ 550C (ICI Equivalent “ TS 220 )

12.  ALFA 150   Working Range  150 “ 550C  (ICI Equivalent  - TS 150 )

ALFA  150 can be used for MARTEMPERING &  AUSTEMPERING of steels.